Spherical Titanium Powder

Spherical Titanium Powder and Titanium Alloy Powder

The Titanium powder and Titanium-based alloy powder are high purity and good density. These are basic powder materials for metal 3D printing (laser/electron beam selective melting), aerospace key components, and biomedical titanium alloy implants (surface treatment).

We can provide kinds of titanium alloy powders with customized sizes. If you can't find what you are looking for, please feel free to contact us via email.

Grade: TA0/Ti/Cp，TA1/Gr.1，TC4/Ti64/Gr.5，TC4 ELI，TC11/BT9，TC17，TC18，TC21，TA7，TA12，TA15/BT20，TA17，TA19/Ti6242，Ti40，Ti60，TiAl（Ti36Al,Ti48Al2Cr2Nb/Ti4822），TiNi，TiNb，ZrTi

Standard: GB/T 3620.1, GB/T 3620.2, GB/T 4698, ASTM F2924, ASTM F3001, ASTM F3187, AMS 4998, AMS 4999, GB/T 1480, GB/T 5329, GB/T 8180

Particle size: 0-20μm, 15-45μm, 15-53μm, 53-105μm, 53-150μm, 105-250μm

Shape: Spherical, Ψ0≥0.90

Appearance: Gray

3D Printing Application: SLM, EBM, LMD

Other Application: PM, MIN, HIP, SP, Welding repair

Package: Vacuum packaging (aluminum foil bag) or argon-filled protective packaging (Aluminum bottle)

Properties of Pure Titanium Powders

Particle Size Range (um)	Laser Particle Size Distribution (um)			Apparent Density (g/cm3)	Carney Flow (s/50g)	Hall Flow (s/50g)	Oxygen Content (ppm)	Nitrogen Content (ppm)
Particle Size Range (um)	D10	D50	D90	Apparent Density (g/cm3)	Carney Flow (s/50g)	Hall Flow (s/50g)	Oxygen Content (ppm)	Nitrogen Content (ppm)
0-15	6	15	21	2.1	/	/	800-1100	≤100
15-53	18	35	49	2.3	≤6	≤36
53-105	64	73	108	2.5	≤5	≤35

Mechanical Properties of Titanium Alloy Powder

Grade	Mechanical Properties
Grade	σb（MPa）	σ0.2（MPa）	δ（%）
TC4/Ti64/Gr.5	1040-1130	950-1010	8-18
	950-1130	830-1080	9-12
	≥895	≥825	≥8-10
TC11/BT9	1080-1150	910-1030	6-15
TC11/BT9	≥1030	≥910	≥8
TA15/BT20	950-1200	855-970	8-14
TA15/BT20	≥930	≥855	≥8~10

Chemical Composition Of Titanium Alloy Powder

Grade	Chemical Composition (wt.%)
Grade	Ti	Fe	Al	V	C	N	H	O	Si	Zr	Mo	Cr
Commercially Pure Titanium	Bal.	≤0.10			≤0.08	≤0.03	≤0.015	≤0.15	≤0.08
Ti6Al4V	Bal.	≤0.30	5.50-6.75	3.50-4.50	≤0.08	≤0.03	≤0.015	≤0.12
TA15/BT20	Bal.	≤0.25	5.50-7.10	0.80-2.5	≤0.08	≤0.05	≤0.015	≤0.15	≤0.15	1.5-2.5	0.50-2.0
TC11/BT9	Bal.	≤0.25	5.80-7.00		≤0.08	≤0.05	≤0.01	≤0.15	0.20-0.35	0.80-2.00	2.80-3.80
TC18	Bal.	0.5-1.5	4.4-5.7	4.0-5.5	≤0.08	≤0.05	≤0.015	≤0.18	≤0.15	≤0.30	4.0-5.5.5	0.5-1.5

Properties of TC4 Powders

Particle Size Range (um)	Laser Particle Size Distribution (um)			Apparent Density (g/cm3)	Carney Flow (s/50g)	Hall Flow (s/50g)	Oxygen Content (ppm)	Nitrogen Content (ppm)
Particle Size Range (um)	D10	D50	D90	Apparent Density (g/cm3)	Carney Flow (s/50g)	Hall Flow (s/50g)	Oxygen Content (ppm)	Nitrogen Content (ppm)
0-15	7	13	21	2.1	/	/	800-1600	≤300
15-53	20	33	49	2.4	≤6	≤35
53-105	65	75	119	2.5	≤5	≤25
105-150	108	131	158	2.4	≤5	≤25

Custom Products - Properties of Ti2AlNb Powders

Particle Size Range (um)	Laser Particle Size Distribution (um)			Apparent Density (g/cm3)	Carney Flow (s/50g)	Hall Flow (s/50g)	Oxygen Content (ppm)	Nitrogen Content (ppm)
Particle Size Range (um)	D10	D50	D90	Apparent Density (g/cm3)	Carney Flow (s/50g)	Hall Flow (s/50g)	Oxygen Content (ppm)	Nitrogen Content (ppm)
15-53	20	36	50	2.5	≤6	≤60	800-1300	≤200
53-105	68	75	110	2.9	≤5	≤50	800-1300	≤200